Alloy 20 Buttweld Pipe Fittings

As an acclaimed enterprise of the industry, Sunrise Steel Centre is involved in offering a vast array of Alloy 20 Butt Weld Pipe Fittings as a manufacturer, exporter, stockiest and supplier to our domestic and global clients. With respect to different grades, we offer these Carpenter 20 Pipe Fittings in different types such as Alloy 20 Seamless Butt weld pipe fittings, Alloy 20 Welded Butt weld pipe fittings, Alloy 20 Elbow (45deg, 90deg, 180deg), Alloy 20Equal & Unequal (reducing) Tees, Alloy 20 Equal & Unequal (reducing) Cross, Alloy 20 Concentric & Eccentric Reducer, Alloy 20 Long & Short Stubends, and Alloy 20 Pipe End Caps.

DIN 2.4660 Alloy 20 Long Radius Elbow, Alloy 20 Swage Nipple, UNS N08020 Concentric Reducers, Alloy 20 Stub Ends, ANSI B16.9 Alloy 20 Crosses Suppliers.

ANSI B16.9 Alloy 20 Buttweld Pipe Fittings Specification

Standard : ASTM / ASME / ANSI

Dimensions : ASME / ANSI B16.9, B16.11, B16.28, B16.5, MSS SP-43, GB12459, GB/T13401, GB/T14383, SH3406, SH3408, SH3409 etc. .

Specifications : ASTM B 366 / ASME SB 366

Grade : Alloy 20 – UNS N08020

Alloy 20 Seamless Butt Weld Fittings Size : 1/2″ – 10″

Alloy 20 Welded Butt Weld Fittings Size : 1/2″ – 48″

Wall Thickness : From 2 to 40 mm.

Schedule : Sch 5 TO Sch XXS.

Type : Seamless / ERW / Welded / Fabricated

Alloy 20 Pipe Fittings Chemical Composition

Element	Alloy 20
Ni	32 – 38
Fe	Bal
C	0.02 max
Mn	1 – 2
Si	0.7 max
Cu	3 – 4
Cr	19 – 21
Mo	2 – 3
S	0.005 max
P	0.02 max
Nb	0.1 – 0.3

Alloy 20 Buttweld Pipe Fittings Physical & Mechanical Properties

Element	Alloy 20
Density	8.1 g/cm3
Melting Point	1443 °C (2430 °F)
Tensile Strength	Psi -80,000, MPa -551
Yield Strength (0.2%Offset)	Psi – 35,000, MPa – 241
Elongation	30 %

Click to enlarge

Back to products

Compare

Add to wishlist

Categories: Alloy 20 Buttweld Pipe Fittings, Alloy 20 Products Tags: Alloy 20, Alloy 20 Buttweld Pipe Fittings, Buttweld Pipe Fittings, Pipe Fittings

Description

Element	Alloy 20
Ni	32 – 38
Fe	Bal
C	0.02 max
Mn	1 – 2
Si	0.7 max
Cu	3 – 4
Cr	19 – 21
Mo	2 – 3
S	0.005 max
P	0.02 max
Nb	0.1 – 0.3

Element	Alloy 20
Density	8.1 g/cm3
Melting Point	1443 °C (2430 °F)
Tensile Strength	Psi -80,000, MPa -551
Yield Strength (0.2%Offset)	Psi – 35,000, MPa – 241
Elongation	30 %